Extra Strength Where Bags Need It Most
The weakest point on a handbag is the base of the handle, where the fabric endures the most stress. Standard PP woven fabric tears at around 80 N in the warp direction. Our PP Laminated Woven Fabric exceeds 120 N. We increased the weave density from the usual 12×10 ends per inch to 14×12, adding strength without significantly increasing weight-only 20–30 g/m² extra. This gives you more durability without making the bag heavier.
Tested With 10 kg for 72 Hours
We perform a practical load test on every batch. A 30 cm × 30 cm piece is fixed at the four edges, and a 10 kg weight is hung in the center for 72 hours. The fabric must not tear. Full specifications compared to standard bag fabric:
|
Parameter |
Handbag Grade |
Regular Bag |
|
Tear Strength (Warp) |
≥120 N |
≥80 N |
|
Tear Strength (Weft) |
≥100 N |
≥70 N |
|
Weave Density |
14×12 ends/inch |
12×10 ends/inch |
|
Weight |
340–420 g/m² |
280–380 g/m² |
Durable Surface for Long-Term Use
Customers often ask about surface wear. We perform a Martindale abrasion test: this fabric withstands over 20,000 cycles while maintaining a good appearance. Nanping Jinwei handles every step in-house, from plastic granules to finished rolls, ensuring consistent quality. Minimum order is 500 meters, with custom samples available in 14 days and a 30-day quality guarantee. Handbags and laptop bags made from our PP Laminated Woven Fabric can carry heavy loads without compromise.